Optical properties of spin-coated Er-doped Ga1As39S60 Chalcogenide thin films
Roshanak Asadi Tabrizi *, Mohammad Rezvani
Tabriz University , roshanak.assadi@gmail.com
Abstract:   (708 Views)
Spin-coating of Chalcogenide glasses is a cost-effective and flexible method to produce thin films applicable in photonics. In this paper Er was doped into Ga1As39S60 glass by melt quenching technique and solutions for spin coating were prepared from glass powders dissolved in Propylamine and Ethylendiamine. Substrates used were microscopic slides (refractive index of about 1.51). Applied layers were dried in 60  vacume for 60 min and then heat treated at 150  for 60 min in Nitrogen Atmosphere. Influence of solvent type on optical parameters of films and the amount of residual solvent was studied by examining UV visible infrared spectroscopy. According to AFM images, surface roughness of layers was about 3.3-3.5 nm. Although films demonstrated PL emission at 1.55 µm, emission intensity was higher at the films deposited from PA solvent. EDS mapping images showed no clusters of Er within the glass matrix.
Keywords: Thin films, Chalcogenide, Spin-Coating, Optical Properties, Solvent
Full-Text [PDF 417 kb]   (70 Downloads)    
Type of Study: Research | Subject: Glass- Glass-Ceramics
Received: 2022/08/2 | Accepted: 2022/09/21 | Published: 2022/05/31
Send email to the article author

Add your comments about this article
Your username or Email:


XML     Print

Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Asadi Tabrizi R, Rezvani M. Optical properties of spin-coated Er-doped Ga1As39S60 Chalcogenide thin films. Jicers 2022; 18 (1) :77-84
URL: http://jicers.ir/article-1-430-en.html

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Volume 18, Issue 1 (Journal of Iranian Ceramic Society 2022) Back to browse issues page
فصلنامه سرامیک ایران Journal of Iranian Ceramic Society
Persian site map - English site map - Created in 0.06 seconds with 30 queries by YEKTAWEB 4570